Hot compression tests of the extruded 7075Al/15%SiC (volume fraction) particle reinforced composite prepared by spray deposition were performed on Gleeble?1500 system in the temperature range of 300?450 °C and strain rate range of 0.001?1 s?1. The results indicate that the true stress?true strain curve almost exhibits rapid flow softening phenomenon without an obvious work hardening, and the stress decreases with increasing temperature and decreasing strain rate. Moreover, the stress levels are higher at temperature below 400 °C but lower at 450 °C compared with the spray deposited 7075Al alloy. Superplastic deformation characteristics are found at temperature of 450 °C and strain rate range of 0.001?0.1 s?1 with corresponding strain rate sensitivity of 0.72. The optimum parameters of hot working are determined to be temperature of 430?450 °C and strain rate of 0.001?0.05 s?1 based on processing map and optical microstructural observation.
采用Gleeble-3500热模拟试验机对15%Si CP/8009铝基复合材料在温度为400~550℃和应变速率为0.001~1 s^(-1)条件下的热变形流变行为进行研究。结果表明:流变应力在开始阶段随应变的增加而增大,出现峰值后逐渐趋于平稳;流变应力随温度的升高而降低,随应变速率的增大而升高,呈现出正应变速率敏感性;流变应力行为可以用双曲正弦模型来描述,其热变形激活能为488.3853 k J/mol,应力指数为7.19022。