A new metal-organic polymer Mn3(BTC)2(H2O)9·(H2O) was synthesized by reaction of the metal ions Mn(Ⅱ) with 1,3,5-benzenetricarboxylic acid(H3BTC) in a mixed solution of DMF/C2H5OH/(H2O) and crystallized.The crystal belongs to monoclinic system,space group C2/c with a=1.901 4(4) nm,b=0.740 23(15) nm,c=2.044 9(4) nm,β=97.18(3)°,V=2.855 5(10) nm3,Z=4,Dc=1.766(g/cm3),μ(Mo Kα)=1.401 mm-1,R[I>2σ(I)]=0.072 7,wR=0.235 1 for 2 419 independent reflections with goodness-of-fit 1.046. Its structure possesses bilayer architectures constructed from Mn ions linked infinite Mn(BTC) chains which were build up from BTC ligand as the "T-shape" module and Mn as the linear module.The hydrogen-bond and π-π stacking interactions between bilayers make them three-dimensional channel-like interpenetrated frameworks.
The title compound Mn 3(BTC) 2(DMF) 4 (BTC=1,3,5-benzenetricarboxylic acid,DMF=dimethyl formamide) was synthesized under the mild conditions and its crystal structure was determined by single crystal X-ray diffraction. The compound crystallizes in the monoclinic system and belongs to space group P2 1/c with a =1.787 6(4) nm, b =1.179 7(2) nm, c =1.884 8(4) nm, β =116.35(3)°, V = 3.561 9(12) nm 3, Z =4, D c=7.413 Mg/m 3, M r=871.43, μ =5.081 mm -1 , F (000)=8 082, R = 0.045 6 , wR =0.106 3. Its structure reveals that each asymmetric unit of the title polymer contains three Mn(Ⅱ) ions,six BTC and four DMF ligands. The coordination of BTC ligands with Mn(Ⅱ) ions forms a 3D infinite framework having helical chains composed with 2 1 axes and about 0.6 nm× 0.8 nm channels along the [100] direction.