The crystallization behavior and kinetics of CaO-MgO-Al2O3 SiO2（CMAS） glass with the Fe2O3 content ranging from zero to 5%were investigated by differential scanning calorimetry（DSC）.The structure and phase analyses were made by Fourier transform infrared spectroscopy（FT-IR） and X-ray diffraction（XRD）.The experiment results show that the endothermic peak temperature about 760℃ is associated with transition and the exothermic peak temperature about 1000℃ is associated with crystallization.The crystallization peak temperature decreases with increasing the Fe203 content.The crystallization mechanism is changed from two-dimensional crystallization to one-dimensional growth,and the intensity of diopside peaks becomes stronger gradually.There is a saltation for the crystallization temperature with the addition of 0.5%Fe2O3 due to the decomposition of Fe2O3.Si-O-Si,O-Si-O and T-O-T（T=Si,Fe,Al） linkages are observed in Fe2O3-CaO-MgO-Al2O3-SiO2 glass.