（TiB2＋TiC）/Ni3Al composites were prepared by mechanical alloying of elemental powders and subsequently spark plasma sintering.Microstructure of（TiB2＋TiC）/Ni3Al composite sintered at 950°C was finer than that of composite sintered at 1050°C.The influence of grain size on cyclic oxidation behavior was investigated.Cyclic oxidation results showed that the composite sintered at 950°C had smaller mass gains than the composite sintered at 1050°C.XRD and EDS results indicate that finer grain size is beneficial for increasing the oxidation resistance by improving the formation of a continuous TiO2 outer layer and a continuous Al2O3 inner layer on the surface of the composites sintered at 950°C.