Polymer solar cells (PSCs) made by poly(3-hexylthiophene) (P3HT) with multi-adducts fullerenes, [6,6]-phenyl-C61-butyric acid methyl ester (PC61BM), PC61BM-bisadduct (bisPC61BM) and PC61BM-trisadduct (trisPC61BM), were reported. Electrochemistry studies indicated that PC61BM, bisPC61BM and trisPC61BM had step-up distributional lowest unoccupied molecular orbital (LUMO) energy. PSCs made by P3HT with above PC61BMs show a trend of enlarged open-circuit voltages, which is in good agreement with the energy difference between the LUMO of PC61BMs and the HOMO of P3HT. On the contrary, reduced short-circuit currents (Jsc) were observed. The investigation of photo responsibility, dynamics analysis based on photo-induced absorption of composite films, P3HT:PC61BMs and n-channel thin film field-effect transistors of PC61BMs suggested that the short polaron lifetimes and low carrier mobilities were response for reduced Jsc. All these results demonstrated that it was important to develop an electron acceptor which has both high carrier mobility, and good compatibility with the electron donor conjugated polymer for approaching high performance PSCs.
A solution-processed zinc oxide (ZnO) thin film as an electron collection layer for polymer solar cells (PSCs) with an inverted device structure was investigated. Power conversion efficiencies (PCEs) of PSCs made with a blend of poly(3-hexylthiophene) (P3HT) and [6,6]-phenyl C61-butyric acid methyl ester (PCBM) are 3.50% and 1.21% for PSCs with and without the ZnO thin film, respectively. Light intensity dependence of the photocurrent and the capacitance-voltage measurement demonstrate that the increased PCEs are due to the restriction of the strong bimolecular recombination in the interface when a thin ZnO layer is inserted between the polymer active layer and the ITO electrode. These results demonstrate that the ZnO thin film plays an important role in the performance of PSCs with an inverted device structure.
YANG TingBinQIN DongHuanLAN LinFengHUANG WenBoGONG XiongPENG JunBiaoCAO Yong