The present work found the plastic deformability of Zr65Cu17.5Ni10Al7.5 BMG dependent on the cooling rate during the formation from the molten state alloy. The deformation behavior in the compression test of φ 2 mm Zr65Cu17.5Ni10Al7.5 BMGs as-cast or lathed from different sizes as-cast samples was characterized, and they exhibited different plastic strains. The compressive plastic strain increases with the decreasing diameter of the as-cast specimens, i.e. with increasing the cooling rate. It is suggested that free volume content in the BMGs, which is related to the cooling rate during the rapid solidification, could play an important role in the deformation process of the BMGs.
ZHANG Jing, PANG ShuJie & ZHANG Tao Key Laboratory of Aerospace Materials and Performance (Ministry of Education), Department of Materials Science and Engineering, Beijing University of Aeronautics and Astronautics, Beijing 100191, China
Bulk metallic glasses (BMGs) with large supercooled liquid region are promising materials for superplastic forming. In this paper, we demonstrate a microstructure-based strategy to pinpoint the composition with the largest supercooled liquid region in La 86 x Al 14 Cu x (x=16 at%-20 at%) metallic glass system. By monitoring the changes in crystallization behavior of the glassy alloys with composition to search for the alloys exhibiting eutectic crystallization, the glassy alloys with the largest supercooled liquid region in the given alloy system can be found. The metallic glasses with Cu contents of 16 at%-19 at% exhibited two crystallization peaks, and the primary crystallization product was identified to be α-La by means of DSC, XRD and TEM. The increase in Cu content resulted in the decay of the primary crystallization peak and the increase in onset temperature of crystallization, leading to the enlargement of supercooled liquid region. By further suppressing the α-La primary crystallization with increasing Cu content up to 20 at%, the eutectic crystallization of α-La and LaCu 13 through one crystallization reaction occurred upon heating, where the largest supercooled liquid region of 65 K for La 66 Al 14 Cu 20 glassy alloy was located. This study indicats that, in a given glassy alloy system, a larger supercooled liquid region can be achieved by optimizing the alloy compositions to suppress the primary crystallization.