Titanium silicate-1(TS-1) was treated with a mixed alkaline of tetrapropyl ammonium hydroxide(TPAOH) and NaOH. It was characterized by XRD, nitrogen physical adsorption, SEM, FT-IR, UV-Vis and ICPOES, and studied in propylene epoxidation. The mixed alkaline treatment with TPAOH/NaOH solution did not destroy the MFI structure of TS-1. With increasing NaOH concentrations, the relative crystallinity and the framework titanium decreased to some extent while the mesopore volume, mesopore diameter, and extra-framework titanium increased appreciably. When NaOH concentration was 0.0333 mol L^(-1), the best catalytic performance was obtained.
Yaquan WangHaoyang LiWei LiuYongjie LinXinpeng HanZhao Wang
ZSM-5 aggregates consisting of superfine and hierarchical nanocrystals(combined with micropores and intra-crystalline mesopores) with an average size of 30 nm were prepared through one-pot synthesis with the assistance of anionic polyacrylamide(APAM). The resultant zeolites(AHN-ZSM-5) were characterized by XRD, ICP-OES, SEM, TEM, BET, NH_3-TPD, Py-IR, and TG analyses and evaluated in the methanol to gasoline(MTG) reaction. Characterization results show that the hierarchical ZSM-5 aggregates possessed two kinds of mesopores, namely inter-and intra-crystalline mesopores. The amount of APAM considerably influenced the mesoporosity and textural properties of AHN-ZSM-5 zeolites. With the addition of APAM in the synthesis, the AHN-ZSM-5 zeolites exhibited large mesopore volume, large external surface area, and appropriate acidity. When applied in the MTG reaction, AHN-ZSM-5 demonstrated a catalytic lifetime that was 1.6 times longer than that of conventional ZSM-5 synthesized in the absence of APAM.
Yaquan WangChunyang FanHongyao LiXiao WangFanjun MengChao SunLiying Sun
SAPO-34, a silicoaluminophosphate zeolite, has been synthesized by the hydrothermal method with the addition of different molecular weights of polyethylene glycol(PEG), and has been characterized with XRD, SEM,N_2 adsorption–desorption, FT-IR, and NH_3 temperatureprogrammed desorption(NH_3-TPD). We studied SAPO-34 as a catalyst in the methanol-to-olefins(MTO) reaction, in a fixed-bed reactor. The results show that the chain length of PEG has a great influence on the particle size and morphology of SAPO-34. PEG acts as inhibitor in the crystallization process. With the increase of the chain length of PEG used in the synthesis, from a relative molecular weight of 400-6000, the morphology of SAPO-34 changes gradually from cubic to nanoplate-like and then changes to cubic again. The particle size decreases markedly at first and then increases to some extent. The catalytic stability in the MTO reaction also increases first and then decreases, with all the catalysts having almost the same selectivity to olefins. When the sample is synthesized with PEG800, the particles become nanoplate-like with a thickness of 46 nm on average, and the catalytic stability is appreciably prolonged, which is attributed to the shorter diffusion paths of the reactants in the zeolite.
Yaquan WangZhao WangChao SunHengbao ChenHongyao LiHaoyang Li
TS-1/SiO_2 extrudate was post-treated with mixed solution of tetrapropyl ammonium hydroxide(TPAOH)and various ammonium salts solution(NH_4F,(NH_4)_3PO_4,(NH_4)_2CO_3,(NH_4)_2SO_4,NH_4CH_3CO_2,NH_4NO_3,NH_4Cl and(NH_4)_2TiF_6).The obtained hierarchical TS-1 catalysts were characterized by many techniques and tested for propylene epoxidation using hydrogen peroxide as an oxidant in a fixed-bed reactor.It was shown that the physicochemical and catalytic properties of the treated TS-1/SiO_2 extrudate depended on the types of ammonium salts added.Compared to the treatment with TPAOH alone,the treatment with a mixed solution of TPAOH and some ammonium salts can greatly improve the catalytic properties of the treated TS-1/SiO_2 extrudate.Some of these ammonium salts were favorable for the incorporation of titanium in the framework,and the beneficial effect depended on the types of ammonium salt.TS-1/SiO_2 extrudate treated with a mixed solution of TPAOH and(NH_4)_3PO_4 exhibited the highest catalyst stability in propylene epoxidation.Such catalytic property can be correlated to high crystallinity,more framework titanium,large specific surface area and large external surface area.