A series of K3Gd1-x-y（PO4）2：xCe^3＋, yTb^3＋ phosphors are synthesized by the solid-sate reaction method. X-ray diffraction and photoluminescence spectra are utilized to characterize the structures and luminescence properties of the as-synthesized phosphors. Co-doping of Ce^3＋ enhances the emission intensity of Tb^3＋ greatly through an efficient energy transfer process from Ce^3＋ to Tb^3＋. The energy transfer is confirmed by photoluminescence spectra and decay time curves analysis. The efficiency and mechanism of energy transfer are investigated carefully. Moreover, due to the non- concentration quenching property of K3Tb（PO4）2, the photoluminescence spectra of K3Tb1-x（PO4）2：xCe^3＋ are studied and the results show that when x = 0.11 the strongest Tb^3＋ green emission can be realized.
A novel red-emitting phosphor, CaYA1307： Eu^3＋, Sm^3＋, is synthesized by a combustion method at a low temperature （850 ℃）, and the single phase of CaYA1307 is confirmed by powder X-ray diffraction measurements. The photoluminescence property results reveal that the red emission intensity of Eu^3＋ is strongly dependent on the Sm^3＋ concentration. Only the Eu^3＋ luminescence is detected in the Eu^3＋-Sm^3＋ co-doped CaYA1307 phosphor with 393 nm excitation. However, under the characteristic excitation （402 nm） of Sm^3＋, not only the Sm^3＋ emission but also the Eu^3＋ emission are observed. A possible mechanism of the energy transfer between Sm^3＋ and Eu3＋ is investigated in detail.
The structure and photoluminescence （PL） properties of Sr3 SiO5： Sm3＋ and Li＋-doped Sr3SiOs： Sm3＋ red-emitting phosphors were investigated. Samples were prepared by the high-temperature solid-state method. PL spectra show that the concentration quenching occurs when the Sm3＋ concentration is beyond 1.3 mol% in Sr3SiOs： Sm3＋ phosphor without doping Li＋ ions. The concentration-quenching mechanism can be explained by the electric dipole-dipole interaction of Sm3＋ ions. The incorporation of Li＋ ions into Sr3SiOs： Sm3＋ phosphors, as a charge compensator, improves the PL properties. The lithium ions also suppress the concentration quenching in Sm3＋ with concentration increased from 1.3 tool% to 1.7 tool%.
Monovalent ions Li＋, Na＋, and K＋, as charge compensators, are introduced into CaYA1307： M （M = Eu3＋, Ce~＋） in this letter. Their crystal phases and photoluminescence properties of different alkali metal ions doped in CaYA1307 are investigated. In addition, the influence of charge compensation ion Li＋ which has a more obvious role in improving luminescence intensity on CaYA1307： Eu3＋ phosphor is intentionally discussed in detail and a possible mechanism of charge compensation is given. The enhancement of red emission centered at 618 nm belonging to Eu3＋ is achieved by adding alkali metal ion Li＋ under 393-nm excitation.