The nano powders of LaCrO3 were prepared by a sol-gel route. The heat capacity of LaCrO3 nano powders from 350 to 550 K was measured by DSC method and expressed as： Cpa2CrO3） （±0.112） = 166.844 - 8.500 ×10^-3T- 1.022×10^6T^-2 （J/（mol.K）） （350-550 K）. An EMF measurement assembly was developed with CaF2 as an electrolyte for the galvanic cell. From measured EMF data of the reversible cell, （-） PL La2O3, LaF3, O2 （1 atm）lCaF2O2（1 atm）, LaF3, LaCrO3, Cr2O3, Pt（＋）, and the relevant value of Gibbs free energy, the Gibbs free energy of formation of LaCrO3 was calculated from 700 to 885 K： △G ФaLaCrO3 = -1555.364 ＋ 0.354T （kJ/mol） （700-885 K）. And the Gibbs free energy change of reaction from simple oxides La2O3 and Cr2O3 was calculated to be： AG f Oox（LaCrO3） = -94.758 ＋ 8.530×10^-2T（kJ/mol） （700-885 K）.