In this study,2-[2-(2-methoxyethoxy)ethoxy]acetic acid(MEEAA)was used to modify the surface of barium titanate nanoparticles(BT NPs)to enhance the compatibility and dispersion of the BT ceramic fillers in polymer matrix.A uniform coating layer with a thickness about 2 nm was formed on the surface of BT after modification.The poly(vinylidene fluoride)-hexafluoropropene[P(VDF-HFP)]composites filled with MEEAA-modified BT NPs achieved higher permittivity(∼13 at 3.0 vol%filler)and discharged energy density than that of the untreated BT filled composite.The maximum discharge energy density of 7.8 J/cm^(3)was obtained in the nanocomposites with 3 vol%MEEAA-modified BT NPs at electric field of 425 kV/mm,which is 77%higher than that of 4.4 J/cm^(3)of pure P(VDF-HFP)film at electric field of 420 kV/mm.