In order to improve the surface hardness and wear resistance of Ti and Ti alloy components, an oxygen permeationtreatment (OPT) was developed. The oxygen permeation behaviors of three Ti alloys, TA2, TB5 and TC11, treatedin air with O-P medium at high temperature have been studied. The results show that the O-P treatment cansignificantly improve the surface hardness of Ti alloys. The oxidation mass-gain of β-Ti alloy (TB5) is much higherthan α-Ti alloy (TA2) under the same condition, while α+β Ti alloy (TC11) is the lowest. All the Ti alloys treatedat this condition produce two surface layers: the outer layer consists mainly of TiO2, as well as trace of other oxides,and the inner layer consists of a Ti-O interstitial solid solution formed by the diffusion of oxygen in α crystal latticeThick scales of β Ti alloy (TB5) are easily formed depending mainly on the poor solid solution content of oxygen,while deep solution layer can be formed since partial β phase has been transformed into α phase. The scales of α-βTi alloy (TC11) are very thin and compact. Aluminum-rich zone, as well as deficient zone, is found in oxide layerrs.A crystallographic characterization of oxygen solution layer has been performed and evaluated by crystallographiclattice constant.
Hongyan MA, Maocai WANG and Weitao WUState Key Laboratory for Corrosion and Protection, Institute of Metai Research, Chinese Academy of Sciences, Shenyang 110016, ChinaGraduate School of the Chinese Academy of Sciences, Beijing 100039, China
The influence of surface pre-treatments, shot-peening (SP) and laser remelting (LR), on oxygen permeation behaviors of titanium alloy TC11 was investigated. Optical microscope, SEM with EDAX, XRD, and microhardness tester were employed to characterize the microstructure, composition and hardness of this alloy. The results show that the surface roughness is increased by shot-peening, and the microstructure with fine-grain can be obtained by LR pre-treatment. The pre-treated samples were oxygen-permeated at (810± 10) ℃ for 10 h in atmospheric air. The outer layer consists essentially of TiO2, trace Ti2 N, Ti3Al and Ti3AlN for the SP pre-treatment and thin oxygen solution layer is found in the subsurface layer. As for LR pre-treatment, the outer layer consists mainly of TiO2 and small amounts of TiO, and the inner layer consists of alpha crystals, rich in interstitial atoms. Samples by LR pre-treatment has thicker hardened layer with higher hardness values in comparison with SP pre-treated ones.The boost diffusion of oxygen and hardening mechanisms were discussed based on the experimental results.