压水堆(pressurized water reactor,PWR)核电站一次侧运行水化学的优化控制是减少辐射剂量,防止关键设备腐蚀损伤,保持燃料性能的最经济、最有效的途径之一,其本质是通过水化学与设备材料的交互作用改善材料表面氧化膜的特性.综述了PWR核电站一次侧主冷却剂水化学与设备材料腐蚀损伤关系的研究现状及问题,介绍了近年来在PWR一次侧注Zn水化学(Zn-injected water chemistry,ZWC)方面的应用基础研究进展.
Electrochemical noise data in the presence of different corrosion types were analyzed. A correlation between the corrosion type of the observed noise and the entropy rate was recognized. A sequence was transformed from each set of original electrochemical noise signal, then the Markov process M and stationary distribution μ were calculated. Finally, entropy rate of each sequence was obtained by the definition. From the entropy rate, it has been observed that local corrosion showed a lower entropy rate, while uniform corrosion showed a higher entropy rate.
The corrosion process of tinplate in deaerated functional beverage was investigated by using electrochemical impedance spectroscopy (EIS) combined with scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) techniques. The results reveal that the uncoated tinplate shows a poor corrosion resistance and the corrosion type is detinning. During the initial stage of immersion, EIS spectrum consisted of two capacitance arcs with obvious time-constant dispersion effect, which was attributed to the two-dimensional and three-dimensional inhomogeneous distribution of the electrode surface. With the increase of immersion time, the capacitance arc of high frequency shrunk and degenerated, due to the corrosion of tin coating. The pore resistance of tin coating and the charger transfer resistance of substrate, which are determined from the electrochemical equivalent circuit, can be used as the indicators of tinplate corrosion process. The decrease of the pore resistance of tin coating indicates that the corrosion degree of tin layer becomes more severe, whereas the decrease of the charger transfer resistance of substrate implies that the corrosion degree of steel substrate also becomes more severe as the immersion time prolongs.
The degradation process of organosol coated tinplate in beverage was investigated by electrochemical noise (EN) technique combined with morphology characterization.EN data were analyzed using phase space reconstruction theory.With the correlation dimensions obtained from the phase space reconstruction,the chaotic behavior of EN was quantitatively evaluated.The results show that both electrochemical potential noise (EPN) and electrochemical current noise (ECN) have chaotic properties.The correlation dimensions of EPN increase with corrosion extent,while those of ECN seem nearly unchanged.The increased correlation dimensions of EPN during the degradation process are associated with the increased susceptibility to local corrosion.