The texture inhomogeneity in cross shear rolled grain oriented Si steel was investigated by means of the through thickness texture analysis. For the chosen rolling reductions (55%, 66.5%) and mismatch speed ratios (1.0, 1.1, 1.3), the deformation textures in various thickness layers consist of three major components, i.e. strong γ-fiber, medium α-fiber and weak η-fiber, and they show an asymmetrical distribution throughout the thickness. The effect of reduction on the texture gradient is found to be more significant at and near the center layer; however, the effect of mismatch speed ratio is less important. In most cases, a strong {111}<112> texture component appears in the subsurface layers, that may favour the formation of a sharp Goss texture during the subsequent annealing.
Commercial grain oriented silicon steel was cold rolled to thickness from 0.06 to 0.10 mm by cross shear rolling, then annealed in vacuum or a hydrogen atmosphere furnace. Deformation textures of the sheets were researched by ODF method and reverse pole figure quantitative analyses. The results indicate that: in the condition of the cross shear rolling, the deformation texture of rolled sheet is generally similar to that of conventional rolled sheet, however, the texture distribution through the thickness is asymmetrical. With mismatch speed ratio increasing, the amount of Goss texture increases. With reduction ratio increasing, the intensity of γ-fiber becomes strong.
Xiuhua GAO, Kemin QI, Renlong LI, Chunlin QIU, Bo MA and Guangrun BAI (Department of Metal Forming, Northeastern University, Shenyang 110006, China)