Optical emission spectroscopy (OES) was used to study the gas phase composition near the substrate surface during dia-mond deposition by high-power DC arc plasma jet chemical vapor deposition (CVD). C2 radical was determined as the main carbon radical in this plasma atmosphere. The deposition parameters, such as substrate temperature, anode-substrate distance, methane con-centration, and gas flow rate, were inspected to find out the influence on the gas phase. A strong dependence of the concentrations and distribution of radicals on substrate temperature was confirmed by the design of experiments (DOE). An explanation for this de-pendence could be that radicals near the substrate surface may have additional ionization or dissociation and also have recombination, or are consumed on the substrate surface where chemical reactions occur.
在30kW级直流电弧等离子体喷射化学气相沉积(DC Arc P lasm a Jet CVD)设备上,采用Ar-H2-CH4混合气体,通过调节甲烷浓度以及控制其他沉积参数,在Mo衬底上沉积出微/纳米复合自支撑金刚石膜。实验表明,当微米金刚石膜层沉积结束后,在随后的沉积中,随着甲烷浓度的增加,金刚石膜表面的晶粒大小是逐渐减小的。当甲烷浓度达到20%以上时,金刚石膜生长面晶粒呈现菜花状的小晶团,膜体侧面已经没有了粗大的柱状晶,而是呈现出光滑的断口,对该层进行拉曼谱分析显示,位于1145 cm-1附近有一定强度的散射峰出现。这说明所沉积的晶粒全部变为纳米级尺寸。