In this work, a novel duplex Ni-P/Ni-Mo-P coating upon the aluminum（Al） substrate was synthesized via an electroless plating, i.e., the binary Ni-P coating as a transition layer and the ternary Ni-Mo-P coating on the top. It was found that the duplex coating was of a high hardness,large elastic modulus,low porosity and excellent corrosion resistance. In addition, experimental results revealed that for a total 20 μm coating thickness, the duplex coating with a 7 μm of the Ni-Mo-P coating exhibited the best corrosion resistance in 0.5 mol/L sulfuric acid solution, which was attributed to its compact structure and low porosity. This duplex Ni-P/Ni-Mo-P coating with a thin ternary Ni-Mo-P layer is expected to solve the problem of low deposition rate of ternary alloy coating and thereby may expand applications of Al and its alloys in the fields of machine manufacture and corrosion environment.
Gong-Sheng SongShuo SunZhong-Chi WangCheng-Zhi LuoChun-Xu Pan
A kind of sandwich-like NiCo_2O_4/rGO/NiO heterostructure composite has been successfully anchored on nickel foam substrate via a three-step hydrothermal method with successive annealing treatment. The smart combination of NiCo_2O_4, reduced graphene oxide(rGO), and NiO nanostructure in the sandwich-like nano architecture shows a promising synergistic effect for supercapacitors with greatly enhanced electrochemical performance. For serving as supercapacitor electrode, the NiCo_2O_4/rGO/NiO heterostructure materials exhibit remarkable specific capacitance of 2644 mF cm^(-2)at current density of 1 mA cm^(-2),and excellent capacitance retentions of 97.5% after 3000 cycles. It is expected that the present heterostructure will be a promising electrode material for high-performance supercapacitors.