Perovskite-like oxide La2-xSrxCuO4 (x = 0, 1) single crystallites with microrod-like morphologies and tetragonal crystal structures were prepared hydrothermally at 240°C with poly(ethylene glycol) (PEG) or hexadecyltrimethyl ammonium bromide (CTAB) as a surfactant and after calcination at 850°C. The physicochemical properties of the materials were characterized by means of XRD, BET, SEM, TEM/SAED (selected-area electron diffraction), XPS and H2-TPR techniques. It is found that doping Sr2+ to La2CuO4 lattice enhanced the catalytic activity for methane combustion and the LaSrCuO4 catalyst derived from PEG is the best among the tested ones. It is concluded that factors, such as adsorbed oxygen species concentration, reducibility and surface area, determined the catalytic performance of such single-crystalline materials.
Porous S-doped bismuth vanadate with an olive-like morphology and its supported iron oxide(y wt.% FeOx/BiVO4 δS0.08, y =0.06, 0.76, and 1.40) photocatalysts were fabricated using the dodecylamine-assisted alcohol-hydrothermal and incipient wetness impregnation methods, respectively. It is shown that the y wt.% FeOx/BiVO4 δS0.08photocatalysts contained a monoclinic scheetlite BiVO4 phase with a porous olive-like morphology, a surface area of 8.8–9.2 m2/g, and a bandgap energy of 2.38–2.42 eV. There was co-presence of surface Bi5+, Bi3+, V5+, V3+, Fe3+, and Fe2+species in y wt.% FeOx/BiVO4 δS0.08. The 1.40 wt.% FeOx/BiVO4 δS0.08sample performed the best for Methylene Blue degradation under visible-light illumination. The photocatalytic mechanism was also discussed. We believe that the sulfur and FeOx co-doping, higher oxygen adspecies concentration, and lower bandgap energy were responsible for the excellent visible-light-driven catalytic activity of 1.40 wt.% FeOx/BiVO4 δS0.08.
Monoclinic BiVO4 with multiple morphologies and/or porous structures were fabricated using the hydrothermal strategy. The materials were characterized by means of the XRD, Raman, TGA/DSC, SEM, XPS, and UV-Vis techniques. The photocatalytic activities of the BiVO4 materials were evaluated for the degradation of Methyl Orange under visible-light irradiation. It is observed that pH value and surfactant exerted a great effect on the morphology and pore structure of the BiVO4 product. Spherical BiVO4 with porous structures, flower-cluster-like BiVO4, and flower-bundle-like BiVO4 were generated hydrothermally at 100°C with poly(vinyl pyrrolidone) (PVP) and urea (pH = 2) and at 160°C with NaHCO3 (pH = 7 and 8), respectively. The PVP-derived BiVO4 showed much higher surface areas (5.0-8.4 m2/g) and narrower bandgap energies (2.45-2.49 eV). The best photocatalytic performance of the spherical BiVO4 material with a surface area of 8.4 m2/g was associated with its higher surface area, narrower bandgap energy, higher surface oxygen vacancy density, and unique porous architecture.
Haiyan JiangHongxing DaiXue MengLei ZhangJiguang DengYuxi LiuChak Tong Au