A multifunctional material with both electrorheological（ER） performance and luminescence property was synthesized by a simple coprecipitation. The tetrabutyl titanate, as well as the Tb（NO3）3·6H2O and sulphosalicylic acid（C7H6O6S·2H2O, SSA） were chosen as starting materials. The composition, ER performance and luminescence property of the material were studied. The results showed that a novel material（TiTbSSA） with both ER performance and luminescence property was obtained. The relative shear stress τr（τr=τE/τ0, τE and τ0 were the shear stresses of the suspension with and without an applied electric field） of the suspension（30 wt.%） of the material in silicone oil reached 32.7 at a shear rate of 12.5 s–1 and an electric field strength of 4 kV/mm（DC electric field）. The material containing the rare earth（RE=Tb） complex exhibited fine luminescence performance and higher ER activity. Therefore, it is a novel multifunction material which would have wide application prospect.
A two-dimensional（2D）coordination polymer{[Cd（bdc）（dpb）]·H2O}n（1）has been prepared by solvothermal reaction of 1,3-dipyridyl benzene（1,3-dpb）with deprotonated1,4-benzenedicarboxylate（H2bdc）,and was characterized by elemental analysis,IR spectroscopy,and X-ray single-crystal diffraction.It crystallizes in the monoclinic system,space group C2/c with a=15.1839（12）,b=20.7585（17）,c=7.2989（6）,β=117.3450（10）°,V=2043.5（3）3,C24H18N2O5Cd,Mr=526.81,Dc=1.712 g/cm3,F（000）=1056.0,μ=1.110 mm-1and Z=4.The neighboring Cd（II）ions link the bdc2-anions and 1,3-dpb to form an infinite 2D sheet,and such two2D sheets are interlocked with each other to form a 2D→2D sheet.Two groups of interlocked sheets are further linked together by intermolecularπ···πinteraction,giving a 3D supramolecular network.In addition,the fluorescence property of 1 was also studied.