The effects of Manganese （Mn） incorporation on a precipitated iron-based Fischer-Tropsch synthesis （FTS） catalyst were investigated using N2 physical adsorption, air differential thermal analysis （DTA）, H2 temperature-programmed reduction （TPR）, and Mǒssbauer spectroscopy. The FTS performances of the catalysts were tested in a slurry phase reactor. The characterization results indicated that Mn increased the surface area of the catalyst, and improved the dispersion of （α-Fe2O3 and reduced its crystallite size as a result of the high dispersion effect of Mn and the Fe-Mn interaction. The Fe-Mn interaction also suppressed the reduction of （α-Fe2O3 to Fe3O4, stabilized the FeO phase, and （or） decreased the carburization degree of the catalysts in the H2 and syngas reduction processes. In addition, incorporated Mn decreased the initial catalyst activity, but improved the catalyst stability because Mn restrained the reoxidation of iron carbides to Fe3O4, and improved further carburization of the catalysts. Manganese suppressed the formation of CH4 and increased the selectivity to light olefins （C2-4^=）, but it had little effect on the selectivities to heavy （C5＋） hydrocarbons. All these results indicated that the strong Fe-Mn interaction suppressed the chemisorptive effect of the Mn as an electronic promoter, to some extent, in the precipitated iron-manganese catalyst system.
Zhichao TaoYong fangChenghua ZhangTingzhen LiMingyue DingHongwei XiangYongwang Li
A systematic study was undertaken to investigate the effects of the manganese incorporation manner on the textural properties, bulk and surface phase compositions, reduction/carburization behaviors, and surface basicity of an iron-based Fischer-Tropsch synthesis （FTS） catalyst. The catalyst samples were characterized by N2 physisorption, X-ray photoelectron spectroscopy （XPS）, H2 （or CO） temperature-programmed reduction （TPR）, CO2 temperature-programmed desorption （TPD）, and M5ssbauer spectroscopy. The FTS performance of the catalysts was studied in a slurry-phase continuously stirred tank reactor （CSTR）. The characterization results indicated that the manganese promoter incorporated by using the coprecipitation method could improve the dispersion of iron oxide, and decrease the size of the iron oxide crystallite. The manganese incorporated with the impregnation method is enriched on the catalyst＇s surface. The manganese promoter added with the impregnation method suppresses the reduction and carburization of the catalyst in H2, CO, and syngas because of the excessive enrichment of manganese on the catalyst surface. The catalyst added manganese using the coprecipitation method has the highest CO conversion （51.9%） and the lowest selectivity for heavy hydrocarbons （C12＋）.
Tingzhen LiYong YangChenghua ZhangZhichao TaoHaijun WanXia AnHongwei XiangYongwang Li