In this work,the electrochemical behaviors of SAM2X5 Fe-based amorphous alloy coating and hard chromium coating were comparatively studied in 3.5 wt% NaCl solution.In comparison with the hard chromium coating,the SAM2X5 coating exhibited a wider and stable passive region with lower passive current density in the potentiodynamic polarization and showed a considerably lower current density at different anodic potentials in the potentiostatic polarization.In order to understand the passivation mechanism of the Fe-based amorphous coating,the components of the passive films formed at various polarization potentials were examined by X-ray photoelectron spectroscopy.The synergistic effect of Mo,W,Mn and Cr in the passive films was systemically analyzed.It has been revealed that Mo and W facilitate the formation of compact and stable Cr2O3 passive film at lower potentials,and the substantial enrichment of Mn in the passive film enhances the passivation ability at relatively higher potentials.The deep understanding of the passivation characteristics in multicomponent alloy systems could provide a guide for the design of corrosion-resistant amorphous alloy coatings for engineering applications.
The influence of the refilled gas pressure on the glass forming behaviour of one of the best ternary glass forming alloys Zr50Cu40Al10 was studied for the melt spinning process. The amorphicity of as-quenched ribbons was characterized by X-ray diffraction （XRD） and differential scanning calorimetry （DSC）. The refilled chamber atmospheric pressure is crucial to the cooling rate of melt spinning. At high vacuum, at pressure less than 0.0001 atm, fully crystalline fragments are obtained. Monolithic amorphous ribbons were only obtained at a gas pressure of 0.1 atm or higher. The extended contact length between thecribbons and the copper wheel contributes to the high cooling rate of melt spinning. Higher chamber gas pressure leads to more turbulence of liquid metal beneath the nozzle; therefore, lower pressure is preferable at practical melt spinning processes once glass forming conditions are fulfilled.
Hong-wang YangPeng ZhangM.J.TanYuan GeWan-ping TianRui-chun WangRong-de Li
为了分析Al-Y-Fe三元合金的玻璃形成能力和热稳定性,采用熔体急冷法制备了Al(100-2x)YxFex(其中x=3,4,5,6,7,8,9)、Al89Y5Fe6、Al88Y5Fe7和Al87Y5Fe8合金条带.利用x-射线衍射(XRD)及透射电子显微镜(TEM)表征了急冷态和部分晶化后条带的结构,运用示差扫描量热仪(DSC)分析了合金的玻璃转变和晶化行为.结果表明,Al88Y6Fe6、Al84Y7Fe7、Al89Y5Fe6和Al88Y5Fe7可以形成完全非晶合金;Al88Y5Fe7非晶合金280℃等温退火30 min析出纳米尺寸Al晶体,370℃等温退火30 min Al晶体发生进一步长大并有金属间化合物析出.
The high temperature tensile and fracture behavior of Zr50Al40Cu10 metallic glass at the temperature range in the vicinity of glass transition were investigated. Tensile tests were carried out at room temperature, 350-420 ℃, and in the supercooled liquid region temperature range, respectively. Obvious plastic deformation was initiated at temperature about 80 °C lower than the glass transition temperature. The ultimate tensile strength decreases with the increase of testing temperature and the ductility increases with temperature. At temperature higher than Tg, viscous flow of Non-Newtonian fluid led to super plastic deformation behavior. The deformation process under tension was inhomogeneous, and remarkable serrations were observed on the stress-strain curve near glass transition temperature.
Xue-feng GaoNa GeFu-yu DongRui-chun WangHong-wang Yang
为了研究等离子喷涂制备热障涂层(TBCs)时不同枪速对陶瓷面层组织性能和残余应力的影响,在GH4169高温合金基体上采用超音速火焰喷涂(HVOF)Ni Co Cr Al Y粘结层(BC层)和大气等离子喷涂(APS)8YSZ陶瓷层(TC层).通过对比不同参数样品的微观组织以及显微硬度、残余应力和热震性能差异,研究了枪速对热障涂层的影响.结果表明:枪速过低或过高时,涂层表面残余应力较大,热震性能较低;随着枪速的增大,涂层表面粗糙度逐渐增大,而孔隙率和显微硬度逐渐减小;枪速过低时,涂层出现纵向裂纹,热震失效方式为整体剥落;而枪速较大时,涂层从边缘向中心不断剥落,涂层表面出现白点.