In this work, a series of carbon aerogel microspheres（CAMs） with tailored pore structures were successfully prepared via a sol-gel method and subsequent heat-treatment at various temperatures from 600 to 1600 ℃. The effects of heat-treatment temperature（HTT） on the CAM microstructure were systematically investigated by physical and chemical characterization. The electrical conductivity increased by up to 250 S/cm and mesopores with high electrolyte accessibility developed in the CAM with increasing HTT. However, the specific surface area（SSA） decreased for HTTs from 1000 to 1600 ℃. The results show that these two factors should be finely balanced for further applications in high power supercapacitors.The CAMs carbonized at 1000 ℃ had the highest SSA（1454 m^2/g）, large mesoporous content（20%） and favorable conductivity（71 S/cm）. They delivered a high energy density of 38.4 Wh/kg at a power density of 0.17 kW/kg. They retained an energy density of 25.5 Wh/kg even at a high power density of 10.2 kW/kg,and a good rate capability of 84% after 10,000 cycles. This performance is superior to, or at least comparable to, those of most reported carbon materials.