The real time and in situ investigation of the crystallization process and structure transitions of asymmetric crystalline-crystalline diblock copolymers from the melt was performed with synchrotron simultaneous SAXS/WAXS. The asymmetric poly(ethylene oxide)-b-poly(ε-caprolactone) diblock copolymers were chosen for the present study. It was shown that the short blocks crystallized later than the long blocks and final lamellar structure was formed in all of the asymmetric diblock copolymers. The final lamellar structure was confirmed by AFM observation. The SAXS data were analyzed with different methods for the early stage of the crystallization. The Guinier plots indicated that there were no isolated domains formed before the formation of lamellae in the asymmetric diblock copolymers during the crystallization process. Debye-Bueche plots implied the formation of correlated domains during crystallization.
Fei-fei XueXue-si ChenLi-jia AnSergio S. FunariShi-chun Jiang
The crystalline structures and crystallization behaviors of iPP containing β nucleation agent TMB-5(iPP/TMB-5) were investigated by synchrotron radiation wide angel X-ray diffraction(SR-WAXD), differential scanning calorimeter(DSC) and polarized light microscope(PLM). It was found that α-crystallization lagged behind β-crystallization at normal temperatures, but the discrepancy reduced with increasing temperature. TMB-5 could not induce β-iPP when the nucleation agent is wrapped up with α-crystal that crystallized at high temperatures. The polymorphic composition of iPP/TMB-5 was susceptible to the introductory moment of shear. New crystallization process of β-nucleated iPP was proposed to understand the experimental phenomena which could not be explained by those reported in the literature. It was supposed that polymer crystallization initiated from mesophase, and the formations of iPP crystals involved the organization of helical conformation ordering within mesophase. It was proposed that the iPP melt contained mesophases with stereocomplex-type ordering of right-handed and left-handed helical chains which could be disturbed by shear or TMB-5, leading to different polymorphic structures.