The local environment of Cu atoms in Fe73.5Cu1Nb3Si13.5B9 alloy was investigated by extended X-ray absorption fine structure(EXAFS).Cu clusters began to order when the annealing temperature was around 733 K from the results of the Fourier transform curves.The fitting results showed that the first shell of the near fcc(face-centered cubic)Cu clusters only contained Cu atoms.The coordination number increased with the annealing temperature.Subsequently,the occupancy rate increased from 33.3%(annealed at 733 K)to 100% (annealed at 853 K).This local structural change of Cu atoms could probably affect the distribution of the bcc(body-centered cubic)α-Fe in Fe73.5Cu1Nb3Si13.5B9 alloy.
Water-soluble magnetite nanocrystals have been prepared by one-step non-alkoxide sol-gel method.The magnetic properties of magnetite nanocrystals obtained are size dependent.The experimental results also reveal that 2-pyrrolidone not only serves as solvent,but also involves surface coordination which renders the magnetite nanoparticles water-soluble and colloidal solution stable.Although the current synthetic approach is a small modification to the non-alkoxide sol-gel method,it allows us to directly obtain high-quality water-soluble magnetic nanocrystals.In addition,we realize that this method could be easily extended to preparation of many other transition and main group metal oxide water-soluble nanocrystals only from simple metal ion salts.