Pd-MnO_2/TiO_2 nanotube arrays(NTAs) photo-electrodes were successfully fabricated via anodization and electro deposition subsequently; the obtained Pd-MnO_2/TiO_2 NTAs photo electrodes were analyzed by scanning electron microscopy(SEM), X-ray diffraction(XRD) and characterized accordingly. Moreover, the light harvesting and absorption properties were investigated via ultraviolet–visible diffuse reflectance spectrum(DRS); photo degradation efficiency was investigated via analyzing the photo catalytic degradation of Rhodamine B under visible illumination(xenon light). The performed analyses illustrated that Pd-MnO_2 codoped particles were successfully deposited onto the surface of the TiO_2 nanotube arrays;DRS results showed significant improvement in visible light absorption which was between400 and 700 nm. Finally, the photo catalytic degradation efficiency results of the designated organic pollutant(Rhodamine B) illustrated a superior photocatalytic(PC) efficiency of approximately 95% compared to the bare TiO_2 NTAs, which only exhibited a photo catalytic degradation efficiency of approximately 61%, thus it indicated the significant enhancement of the light absorption properties of fabricated photo electrodes and their yield of UOH radicals.